We fabricated a sensing layer from ink-printed WS2 flakes and utilized it for UV-activated gas sensing. The optical imaging of the structure made by repeated printing revealed the continuous layer comprising sub-µm flakes, confirmed independently by small-area AFM images (1×1 µm2). The activity of the sensing surface was investigated locally via AFM scanning of the surface with a polarized probing tip. The results indicated that...

Metal oxide gas sensors are popular chemoresistive sensors. They are used for numerous tasks, including environmental and safety monitoring. Some gas-sensing materials exhibit photo-induced properties that can be utilized for enhanced gas detection by modifying the sensor selectivity and sensitivity when illuminated by light. Here, we present the gas sensing characteristics of highly nanoporous Cu2O thin films towards both electrophilic...

We discuss the implementation challenges of gas sensing systems based on low-frequency noise measurements on chemoresistive sensors. Resistance fluctuations in various gas sensing materials, in a frequency range typically up to a few kHz, can enhance gas sensing by considering its intensity and the slope of power spectral density. The issues of low-frequency noise measurements in resistive gas sensors, specifically in two-dimensional...

This work presents the results of fluctuationenhanced sensing (FES) of selected organic gases by MoS2 sensor fabricated via a simple ink printing method. We demonstrate that low-frequency noise measured under UV irradiation (275 nm) is more sensitive to different gases than measured in the dark. The noise at 1 Hz under UV light increased 3.3, 3.5, 1.6, and 2.9 times for chloroform, tetrahydrofuran, acetonitrile, and acetone ambiances, respectively....

In this work, MoS2 flakes were printed on ceramic substrates and investigated toward 1–10 ppm of nitrogen dioxide (NO2), 2–12 ppm of ammonia (NH3), and 2–12 ppm acetone (C3H6O) under UV light (275 nm). The structure of overlapping MoS2 flakes and UV light assistance affected high responsivity to NO2 when DC resistance was monitored, and superior sensitivity to NH3 was obtained from the low-frequency noise spectra. MoS2 exhibited...