During the low plasticity burnishing process of soft materials such as carbon steel with a hardness of up to 40 HRC (Rockwell grade) a raised structure of the material known as the Jumping Wave forms in front of the tool roll. This phenomenon significantly disturbs the burnishing process, but is very poorly described in the literature. This article presents studies of this phenomenon on the example of burnished 1.0562 steel. The...

Heavily loaded structural elements operating in a corrosive environment are usuallyquickly destroyed. An example of such an element is a ship propeller operating in a seawaterenvironment. This research presents a fatigue resistance test performed on elements operating inseawater. Different processing parameters applied on the samples in particular were compared withthe specimens whose surface had been burnished differently and...

The article presents the results of testing the surface condition of shafts manufactured by a strengthening rolling burnishing process. The shafts with a hardness about 220 HB were burnished with a roller with different force. Researches were carried out with particular attention to the structure of the outflowing material in the tool zone during burnishing process. The article presents the results of the examinations of burnished...

This article represents the results of testing the surface condition of shafts manufactured by the burnishing process. The shafts with a hardness of approximately 62 HRC (Rockwell C). were burnished with a ceramic ball (Si3N4), where the force range was controlled by the means of a hydraulic system. The machining process consisted of hard turning shafts with cubic boron nitride (CBN) inserts, followed by burnishing with the use...

Doradztwo przy doborze technologii wygniatania gwintu M39x4 - h6