The results of properties change of beech wood after drying process are presented. The wood taken to experiments was from northern part of Pomeranian region in Poland. Before the main high temperature drying process using air-steam mixture, wood was initially dried in an open air conditions. The high temperature drying process was conducted at temperature 120oC, humidity 48%, flow rate of drying medium 2.5m/s and atmospheric pressure....

The result of mechanical properties change of selected wood species after drying process under various parameters are presented. The global elasticity modulus and bending strength for steam dried, air-steam mixture dried and air dried samples as reference were measured. It allowed to reveal the effect of wood stream, air-steam mixture and their temperature on mechanical properties of wood. It has been recognized that steam and...

Results of influence of gas-steam mixture drying process on wood mechanical properties are presented. Wood species, namely pine (Pinus sylvestris L.) and beech (Fagus silvatica L.) from the northern part of Pomerania region in Poland, were subject of steam kiln-drying process in a laboratory kiln specially arranged for that reason.

The results of influence gas-steam mixture drying process on time wood drying process are presented. Wood species, namely oak (Quercus L.), beech (Fagus L.), pine (Pinus L.) and spruce (Picea K.) from the northern part of Pomerania region in Poland, were subject of air-steam mixture drying process. Main focus of those tests was to shorten the time of drying process and afterward to check properties of wood.

Results of influence of gas-steam mixture drying process on mechanical properties of material are presented. Wood species, namely oak (Quercus L.), beech (Fagus L.), pine (Pinus L.) and spruce (Picea K.) from the northern part of Pomerania region in Poland, were subject of air-steam mixture drying process in a laboratory kiln especially arranged for that reason. Measurements of the global coefficient of elasticity and bending strength...