Semiconducting Na2O-V2O5-TeO2 glasses with various Na2O contents were melted and subjected to controlled heating to improve conductivity. Topography analysis were performed using confocal microscopy and scanning electron microscopy on both as-quenched and heat-treated samples. X-ray diffraction confirmed the amorphous nature of the samples post-melting, with subsequent heating resulting in the formation of nanocrystallites primarily...

Borophosphosilicate glasses with varying sodium ion concentrations were investigated for their, structural, thermal, and electrical properties. All the obtained glasses were transparent except the glass with the highest sodium content, which exhibited translucency due to inhomogeneities. Increasing sodium content led to reduced boron and silicon content while maintaining a constant B/Si ratio, indicating progressive depolymerization...

V2O5–TeO2 glass–ceramics (VTGC) were prepared by controlled annealing of the V2O5–TeO2 glass (VTG), which illustrates a parent glass matrix with a single charge carrier. The annealing proceeded at six temperatures selected between the glass transition and the maximum of the frst crystallization process to obtain various nanocrystallite sizes. Heat treatment caused an increase in DC conductivity by 2.5–3.5 (250–285 °C) order of...

In the present paper, V 2 O 5 -TeO 2 glass was prepared by the melt-quenching technique. Crystallization of glass with a vanadium content higher than 35%mol results in an increase in electrical conductivity by a few orders of magnitude and a decrease in activation energy from ~0.40 to ~0.12 eV. In this work, a critical review of existing charge transfer models was presented on the example of V 2 O 5 -TeO 2 glass and glass–ceramics....

The disintegration of a continuous metallic thin film leads to the formation of isolated islands, which can be used for the preparation of plasmonic structures. The transformation mechanism is driven by a thermally accelerated diffusion that leads to the minimalization of surface free energy in the system. In this paper, we report the results of our study on the disintegration of gold thin film and the formation of nanoislands...