Multicomponent oxides often have exceptional thermal stability and interesting electronic properties. The present work presents the thermoelectric and electrical properties of the Ba(Zr0.2Hf0.2Sn0.2Ti0.2Fe0.2)O3−δ and Ba(Zr0.1Hf0.1Sn0.1Ti0.1Co0.1Ce0.1Bi0.1Fe0.1Y0.1Zn0.1)O3−δ multicomponent perovskites. Single-phase cubic perovskites were synthesized using the solid-state reaction method. They were characterized using X-ray...

In this work, the chosen physicochemical properties of single-phase multicomponent oxides BaTi1/8Fe1/8Co1/8Y1/8Zr1/8Sn1/8Ce1/8Hf1/8O3-δ and BaTi1/9Fe1/9Co1/9Y1/9Zr1/9Sn1/9Ce1/9 Hf1/9Bi1/9O3-δ were studied. The microstructure of the compounds strongly depended on the presence of bismuth in the structure. The electrical transport studies showed a level of electrical conductivity of ∼10−3 - 10−2 S/cm in the temperature range 673–1073...

In this work, partial protonic conductivity in mixed conducting (BZCY721) and BaGd0.3La0.7Co2O6−d (BGLC137) was studied. For this purpose, a modified DC Hebb–Wagner polarization method was used. A four-wire type of galvanic cell as well as a suitable calculation model was applied. The method was validated using proton conducting electrolyte – BaZr0.7Ce0.2Y0.1O3−d – as a reference material. For the first time, protonic partial conductivity...

In this work, oxidation properties of austenitic 316L stainless steel powder and sintered porous support were investigated at the temperature range of ~600-750 °C for 100 hours in ambient air. Oxidation kinetics was determined by continuous thermogravimetry and analyzed employing parabolic rate law. It was observed that oxidation leads to the formation of an oxide scale, with substantial oxidation occurring at ≥ 650 °C in the powder....

The electrical properties of the entropy stabilized oxides: Zr6Nb2O17, Zr6Ta2O17, Hf6Nb2O17 and Hf6Ta2O17 were characterized. The results and the electrical properties of the products (i.e. ZrO2, HfO2, Nb2O5 and Ta2O5) led us to hypothesize the A6B2O17 family is a series of mixed ionic-electronic conductors. Conductivity measurements in varying oxygen partial pressure were performed on A6Nb2O17 and A6Ta2O17. The results indicate...