Efficient replacement of materials based on critical elements such as cobalt is one of the greatest challenges facing the field of solid oxide cells. New generation materials, free of cobalt show potential to replace conventional materials. However, these materials are characterized by poor ability to block chromium diffusion. This article described the study of CuMn1.7Fe0.3O4 (CMFO) spinel combined with single metal oxide (Y2O3...

MnCo1.5Fe0.5O4 spinel oxide was synthesized using the sol−gel technique, followed by heat treatment at various temperatures (400, 600, 800, and 1000 °C). The prepared materials were examined as anode electrocatalysts for watersplitting systems in alkaline environments. Solid-state characterization methods, such as powder X-ray diffraction and X-ray absorption spectroscopy (XAS), were used to analyze the materials’ crystallographic...

This work evaluates partially amorphous La0.6Sr0.4CoO3-δ (LSC) as a potential oxygen electrode for lowtemperature solid oxide cells. LSC was deposited using the spin-coating technique onto Ce0.8Gd0.2O2-δ (CGO) substrates. The optimal oxygen electrode thickness was determined as 500 nm. The electrochemical impedance spectroscopy (EIS) study showed a significant improvement in oxygen reduction/oxidation reaction kinetics when annealing...

Nanocrystalline cerium (IV) oxides doped with transition metals have gained significant interest recently, mostly in the field of catalysis. Herein, we present the comprehensive studies on ceria doped with 10 mol.% of transition metals (Mn, Fe, Co, Ni or Cu) synthesized by the reverse microemulsion method. The aim of this work is to study the properties of those materials with the use of different complementary methods like XRD,...

A novel one-pot synthesis route leading to the formation of a wormhole-like structure was developed for the successful fabrication of porous YSZ and Ni-YSZ systems. This method involved co-precipitation in the presence of the micelle-forming agents CTAB/Pluronic P123 and crystallising NaCl. The obtained skeletons were mechanically stable and presented almost 50% uniform, open porosity without using any additional pore-formers....